Thermal insulation polyurethane structural bonding adhesive（2.0W）
JOMP2652 (2W) A/B is a two-component solvent-free room temperature curing adhesive with low odor and low The product meets VOC standards and complies with ROHS and REACH regulations . Featuring flexible process adaptability and high physical
properties , it is suitable for both machine dispensing and manual mixing operations . After curing, it exhibits excellent adhesion, strong bonding strength, superior thermal conductivity, along with outstanding resistance to aging and chemical exposure . It is ideal for sealing and bonding applications across various materials including metals, plastics, rubber, and polyester.
product details
Thermal insulation polyurethane structural bonding adhesive
JOMP2652 (2W) A/B is a two-component solvent-free room temperature curing adhesive with low odor and low The product meets VOC standards and complies with ROHS and REACH regulations . Featuring flexible process adaptability and high physical
properties , it is suitable for both machine dispensing and manual mixing operations . After curing, it exhibits excellent adhesion, strong bonding strength, superior thermal conductivity, along with outstanding resistance to aging and chemical exposure . It is ideal for sealing and bonding applications across various materials including metals, plastics, rubber, and polyester.
characteristic
| test item Unit and condition detection criteria A / B | |||||
| surface | visualization | visualization visualization | Yellow viscous fluid | ||
| Green viscous fluid | |||||
| A
B viscosity A + B |
25℃
mPa·s |
GB/T 10247-2008
GB/T 10247-2008 GB/T 10247-2008 |
100000~200000 | ||
| 150000~250000 | |||||
| 150000~250000 | |||||
| A
B A + B |
25℃ g/cm3 |
GB/T 15223-1994
GB/T 15223-1994 GB/T 15223-1994 |
2.20~2.30 | ||
| 2.20~2.30 | |||||
| 2.20~2.30 | |||||
| matching | Volume ratio A: B | 100 ： 100 | |||
| Weight ratio A: B | 100 ： 100 | ||||
| operate time | 25℃min GB/T 6328-86 | 30~50 | |||
| initial setting time | 25℃ min GB/T 6328-86 | 60~ 120 | |||
| Full solidification time | 25℃ d GB/T 6328-86 | 7 | |||
| 25℃ Performance parameters after 7 days of curing | |||||
| project | Unit or condition detection standard | JOMP2652 (2W) | |||
| pigment | Visual inspection. Visual inspection | green | |||
| hardness | Shore D | GB/T 531-2008 | 75±5 | ||
| tensile strength | MPa GB/T 528-2009 | ≥9 | |||
| elongation | % GB/T 528-2009 | ≥ 10 | |||
| shear strength | MPa, Al-Al
|
GB/T 6328-86
|
≥9 | ||
| shear strength | MPa, PET-PET GB/T 6328-86 | ≥5 | |||
| thermal
conductivity |
W/m. K GB/T10297-1998 | ≥2.0 | |||
| DMA modulus | 25℃, MPa IPC-TM-650 | 800 | |||
| mass resistivity | 25℃ , Ω·cm GB/T 1692-92 | ≥ 1013 | |||
| insulation strength | 25℃ , kV/mm GB/T 1695-2005 | 20 | |||
| Application
temperature |
℃ GBT 20028-2005 | -40 ～85 | |||
| Flame retardant rating | UL UL94 | V-0 | |||
Use techniques
Special measurements can be used when mixing. After use, store in a sealed container.
Order packing
JOMP2652 (2W) A/B polyurethane adhesive
Packaging: 400 ml/double tube
Packaging: 5 gallons/barrel
Storage notes
Unused raw materials should be stored in a well-sealed
To avoid moisture intrusion and affect the quality of raw materials. Open materials should be sealed and stored and used up as soon as possible.
This glue is not dangerous goods and can be transported as general chemicals
It is recommended to store in a cool area, avoid direct sunlight; storage temperature: 10-30 ℃, storage period is 6 months.